Precipitation hardening in magnesium alloys
Publication Date
1973
Creator
Abstract
Structural and kinetic aspects of precipitation in the systems Mg-Th and Mg-Nd , with various ternary additions, have been studied, using electron microscopy and electrical resistivity techniques.
The sequence of precipitation in the Mg-Th alloy is solid solution → β" → β. Small additions of manganese and silver have little effect on the precipitation process but additions of zirconium and zinc alter the process significantly. The β” reaction is completely suppressed by an addition of 0.3% zinc and a phase not present in the binary system, β’ Mg2Th, is formed as two polymorphs in the zirconium containing alloy. The sequence of precipitation in the Mg-Nd system is completely changed by the zinc addition. Alloys containing Mg 2.8% Nd 1.3% Zn have the following precipitation sequence Solid solution → low temperature reaction → plates γ”││ (0001) → rods on γ (0001) in <1120> & <1010> The low temperature reaction has not been elucidated but it occurs with an activation energy approximating to that of vacancy migration in magnesium, and may possibly be associated with short range order. The structures of these various alloys have been correlated with their creep and mechanical properties. In particular, the creep properties of the Mg-Nd-Zn alloy have been shown to be superior to those of the binary Mg-Nd alloy and the improvement has been attributed to the γ" phase restricting dislocation motion on the {1011} planes.
The sequence of precipitation in the Mg-Th alloy is solid solution → β" → β. Small additions of manganese and silver have little effect on the precipitation process but additions of zirconium and zinc alter the process significantly. The β” reaction is completely suppressed by an addition of 0.3% zinc and a phase not present in the binary system, β’ Mg2Th, is formed as two polymorphs in the zirconium containing alloy. The sequence of precipitation in the Mg-Nd system is completely changed by the zinc addition. Alloys containing Mg 2.8% Nd 1.3% Zn have the following precipitation sequence Solid solution → low temperature reaction → plates γ”││ (0001) → rods on γ (0001) in <1120> & <1010> The low temperature reaction has not been elucidated but it occurs with an activation energy approximating to that of vacancy migration in magnesium, and may possibly be associated with short range order. The structures of these various alloys have been correlated with their creep and mechanical properties. In particular, the creep properties of the Mg-Nd-Zn alloy have been shown to be superior to those of the binary Mg-Nd alloy and the improvement has been attributed to the γ" phase restricting dislocation motion on the {1011} planes.
Item Type
ethesis
Thesis Type
PhD
Supervisors
Subjects (LC)
Associated Schools / Departments
Department of Mechanical, Materials and Manufacturing Engineering (UK)
eprints ID
14061
UoN Repository URI
Except where otherwise noted, this item's license is described as
File(s)![Thumbnail Image]()
Name
467350.pdf
Type
Full-text
Size
20.04 MB
Format
Adobe PDF
Checksum ()