Magneto-dieletric properties of bismuth substituted barium hexaferrite
Publication Date
December 16, 2011
Creator
Abstract
The work contained within this thesis seeks to address the dielectric and magnetic properties of bismuth substituted barium hexaferrite (composition BaBixFe12-xO19 where x = 0.0, 0.2, 0.5, 0.8, 1.0 and 1.5) across a broad frequency spectrum. This material is potentially of interest in antenna applications (specifically a dielectric resonator antenna) where high permittivity and permeability materials can be exploited to physically minimize the size of antenna devices.
At low frequencies (20Hz - 3MHz) LCR meter based analysis was used to investigate the capacitance and inductance of the materials. The highest measured permittivity at 1MHz was Er = 86.18 - 9.910j, tanδ = 0.11. High frequency (45MHz - 20GHz) permittivity was investigated using a vector network analyser (VNA) and coaxial probe. The highest recorded permittivity at 2.45GHz was Er = 14.69 - 1.664j, tanδ = 0:08. A link between substitution level and permittivity and substitution level and inductance was made at either 1MHz or 2.45GHz. The homogeneity of the samples was explored using a near- field permittivity sensor. This showed small localized variations of permittivity across the surface but not significant enough to adversely effect bulk measurements. A dielectric resonator antenna was fabricated using a bismuth substituted barium hexaferrite sample. Resonant frequencies were identified at 6.6, 9.55 and 13.6GHz and radiation patterns for the system showed agreement with published theoretical results. This confirmed the suitability of the material in this application as a high permittivity material with relatively low loss.
This thesis contributes to scientific knowledge by characterising a broad range of bismuth composition materials across a wide frequency range, investigating the link between permittivity/inductance and doping level and presenting full results. The material has also been characterised using a near-field permittivity technique and used to fabricated a dielectric resonator antenna which have not previously been undertaken.
Item Type
ethesis
Thesis Type
PhD
Supervisors
Subjects (LC)
Associated Schools / Departments
Department of Electrical and Electronic Engineering (UK)
eprints ID
12183
UoN Repository URI
Except where otherwise noted, this item's license is described as
File(s)![Thumbnail Image]()
Name
THESIS-MASTER.pdf
Type
Full-text
Description
LeahRidgwayThesis
Size
26.44 MB
Format
Adobe PDF
Checksum ()