Manufacture and characterisation of bioresorbable fibre reinforced composite rods and screws for bone fracture fixation applications
Publication Date
March 15, 2013
Creator
Abstract
Bioresorbable implants are an attractive alternative to metallic bone fixation devices and offer potential to eliminate some of the clinical challenges with the latter. This work explores the manufacturing of fully bioresorbable fibre-reinforced composite rods and screws for such applications. Poly lactic acid (PLA) and phosphate glass fibres (PGF) were combined to provide mechanical reinforcement and biocompatibility characteristics. Aligned and randomly reinforced PLA/PGF composites were prepared by compression moulding prior to thermomechanical deformation into rod and screw forms. In vitro degradation and mechanical properties retention were investigated in phosphate buffered saline (PBS) at 37°C. The composite rods and screws exceeded published data for bioresorbable implants in their virgin state and were towards the upper range of cortical bone properties. The properties reduced rapidly in an aqueous medium and this was attributed to matrix plasticisation and fibre/matrix disbonding. The degraded samples maintained strength and stiffness close to the lower limits of the cortical bone. Water uptake and mass loss for composites exceeded equivalent values for PLA alone due to water wicking at the fibre/matrix interface. Ion release tests correlated linearly with mass loss profiles confirming that the dominant degradation mechanism was fibre dissolution. The PLA/PGF composites also exhibited good biocompatibility to human osteosarcoma and human mesenchymal stem cells.
Item Type
ethesis
Thesis Type
PhD
Supervisors
Subjects (LC)
Associated Schools / Departments
Faculty of Engineering
eprints ID
14379
UoN Repository URI
Except where otherwise noted, this item's license is described as
File(s)![Thumbnail Image]()
Name
594977.pdf
Type
Full-text
Size
23.91 MB
Format
Adobe PDF
Checksum ()